Monitoring of Beech Glued Laminated Timber and Delamination Resistance of Beech Finger-Joints in Varying Ambient Climates

Abstract

In this study, varying ambient climates were simulated in a test building by changing temperature and relative humidity. Beech glued laminated timber (glulam, Fagus sylvatica, L.) was freshly installed in the test building and monitoring of the change in wood moisture content of the glulam resulting from the variations in climate was carried out. Subsequently, finger-jointed beech specimens were exposed to the variations in relative humidity measured in the course of the monitoring experiment on a laboratory scale, and thus an alternating climate regime was derived from the conditions in the test building. Its influence on the delamination of the finger-joints was evaluated. In addition, it was examined whether beech finger-joints using commercial adhesive systems fulfil the normative requirements for delamination resistance according to EN 301 (2018) and whether different bonding-wood moisture levels have an effect on the delamination of the finger-joints. In the context of the monitoring experiment, there was a clear moisture gradient in the beech glulam between the inner and near-surface wood. The applied adhesive systems showed almost the same delamination resistance after variation of relative humidity. The normative requirements were met by all PRF-bonded and by most PUR-bonded beech finger-joints with higher bonding wood moisture content.

In this study, varying ambient climates were simulated in a test building by changing temperature and relative humidity. Beech glued laminated timber (glulam, Fagus sylvatica, L.) was freshly installed in the test building and monitoring of the change in wood moisture content of the glulam resulting from the variations in climate was carried out. Subsequently, finger-jointed beech specimens were exposed to the variations in relative humidity measured in the course of the monitoring experiment on a laboratory scale, and thus an alternating climate regime was derived from the conditions in the test building. Its influence on the delamination of the finger-joints was evaluated. In addition, it was examined whether beech finger-joints using commercial adhesive systems fulfil the normative requirements for delamination resistance according to EN 301 (2018) and whether different bonding-wood moisture levels have an effect on the delamination of the finger-joints. In the context of the monitoring experiment, there was a clear moisture gradient in the beech glulam between the inner and near-surface wood. The applied adhesive systems showed almost the same delamination resistance after variation of relative humidity. The normative requirements were met by all PRF-bonded and by most PUR-bonded beech finger-joints with higher bonding wood moisture content.